The fabrication of this mirror-finish console table began with the frame being constructed from square stainless steel tubing, cut to the required lengths and prepared to form the four legs. The tabletop was fabricated separately, with the stainless steel sheet bent into its desired shape to create the clean, folded profile of the console. Once the top and legs were prepared, the legs were positioned and welded directly to the underside of the tabletop. The welds were then ca

For Café Sofi, we fabricated a set of custom stainless steel sugar holders designed specifically for the restaurant’s table setting. The brief called for a simple, durable piece that would complement the space while remaining practical for everyday use. The fabrication began with stainless steel sheet, which was accurately cut to size before being formed into the required shape. The sheet was then carefully bent to create the base and sides of each holder, producing the clean

The Sculpt Ice Bucket begins with Grade 304 stainless steel sheet, cut and formed to create the main body and its distinctive sculptural profile. The individual components are carefully shaped before being brought together, ensuring the curved form and proportions remain consistent throughout the fabrication process. The sculptural handles are fabricated separately and formed to the required shape before being positioned and welded onto the body. Once the main components are

The Tidal Jug begins with Grade 304 stainless steel tube, cut to the required length to form the main body of the jug. A circular base plate is then cut to match the diameter of the tube and welded into position, creating the closed base. Next, a section of the upper body is cut out to accommodate the spout. The spout is fabricated and carefully positioned before being welded onto the jug, creating the pouring point. The handle is then bent to the required shape and welded on

The Just Lifted Vase begins with a sheet of Grade 304 stainless steel, spun to form the upper bowl and achieve its rounded profile. The base is fabricated separately by rolling stainless steel sheeting into the required cone shape, carefully forming the taper before preparing it for assembly. Once the two components are aligned, the base is welded to the spun bowl, creating a secure connection between the upper and lower sections. The welded areas are then cleaned and prepare

The coupe cup begins as a sheet of Grade 304 stainless steel, spun to form the rounded coupe profile. The spun cup is then trimmed and prepared before the stem is accurately positioned and welded into place, creating a clean, seamless connection between the two components. Once fabrication is complete, the entire piece is polished through multiple stages to achieve a high-quality mirror finish. The result is a sculptural stainless steel coupe cup with a reflective surface and

The Center of Gravity Dining Table was fabricated entirely from Grade 304 stainless steel, combining a brushed circular tabletop with three mirror-finished cylindrical legs. The process began with the 1200mm diameter tabletop being laser cut from 4.5mm thick Grade 304 stainless steel. Once cut, the edge was prepared and the surface was finished in a brushed finish, creating a consistent directional grain across the tabletop. The three legs were cut from 154mm diameter round s

Yakisugi - Burnt Cedar Wood The fabrication of the Yakisugi Burnt Table began with the Siberian Larch table top. The individual 30mm thick wood pieces were carefully positioned and joined together using dowels, which provided additional alignment and strength between each section. The pieces were then glued together to create a solid, continuous table top. Once the timber had been joined, the required cut-outs for the through legs were carefully marked and cut into the table

The Pillar The manufacturing process began with the table top, fabricated from 2.5mm thick 304 stainless steel. The sheet was measured and cut before being bent and formed to create the table’s clean, structured profile. Careful attention was given to the bends and overall dimensions to ensure the finished top was consistent and accurately shaped. For the legs, 350mm diameter stainless steel tubing was sourced and cut to the required height. Using pre-manufactured tubing allo

In the end, the greatest challenge was not making something complex, but making something feel effortless. After all the noise of forming, welding, grinding, and refining, the final piece needed to appear calm, simple, and inevitable. Although the table presents as a minimal and straightforward object, its fabrication required a high level of technical control and process development. The simplicity of the form places significant emphasis on precision, surface continuity, and

Rule of Threes Dining Table The Rule of Threes dining table began with a simple brief: the client already had the tabletop, and our role was to design, fabricate, and install the supporting base. The three-leg structure was fabricated from 2.5mm thick stainless steel, with each leg carefully formed and finished in a brushed finish. The three individual legs create the defining feature of the piece a balanced, minimal base that gives the table its name: Rule of Threes. Once fa

Final Install The Stumped - Jumbo dining table was manufactured from 304 Grade stainless steel, consisting of a 6mm thick circular tabletop supported by a substantial stainless steel tubular base. The process began with the 6mm thick stainless steel sheet being cut to a 1.3m diameter to form the circular tabletop. The heavy-gauge material was prepared and finished to ensure the tabletop remained flat and consistent throughout the fabrication process. The base was manufactured

Final Install The Over the Edge Coffee Table was manufactured from a single sheet of 4mm thick Grade 304 stainless steel. The construction was designed to avoid multiple assembled sections, allowing the table to be formed from one continuous piece of material and creating a seamless overall structure. The process began with the 4mm 304 stainless steel sheet being measured and cut to the required profile. The complete table shape, including the tabletop and supporting sections

Center of Attention Although the Puffed Up coffee table appears effortless in its design, its manufacture proved to be one of the more technically demanding projects. The process began with the table legs, where the required diameter was not available in standard stainless steel tube. Instead, each leg was rolled from 3mm stainless steel plate, fully welded, carefully dressed into shape, and finished with a brushed grain to achieve a seamless appearance. The base presented th